DESCRIPTION:
"Concrete Finishes" H.S.E. is
a two component 100% solids epoxy coating system designed as
a heavy duty re-surfacer that will fill many cracks and superficial
defects in concrete. In it's cured state, it leaves a smooth
non-porous high gloss finish that will withstand industrial
chemicals and high abrasion.
COLORS:
|
All
colors available including clear |
SHEEN: |
High
gloss |
SOLVENTS:
|
None |
WATER: |
None |
ODOUR: |
Virtually
none |
TENSILE STRENGTH: |
6,830
PSI |
FLEXURAL
STRENGTH: |
11,400
PSI |
COMPRESSIVE
STRENGTH: |
14,225
PSI |
DRYING
TIME: |
14-16
hours @ 70 deg. F |
CHEMICAL RESISTANCE (Immersion):
Deionized Water
Road Salt
Ethanol
MEK
Lactic Acid
Acetic Acid
Sulfuric Acid
Sodium Hydroxide
Sodium Hypochiorite
ABRASION TESTING:
"Concrete Finishes" H.E.S.
2000 was tested by an independent lab for abrasion resistance
and compared to 4 concrete floor coatings.
PROCEDURE:
A standard gardner-style scrup tester,
using diamond grit no. 220 wet abrasion paper, kept wet and
changed every 1000 cycles. Cycle to fail indicates the number
of abrasive cycles to wear through the coating film (10mm)
and expose one square inch of the concrete substrate.
TEST
RESULTS |
CYCLES
TO FAILURE |
Solvent
Based Alkyd Floor Paint |
128
|
Solvent
Based Urethane |
96 |
Two
Part Water Based Epoxy |
224 |
Two
Part Solvent Based Epoxy |
1,024 |
Concrete
Finishes H.S.E. 2000 |
6,992 |
CONCLUSION:
Concrete Finishes H.S.E. 100% Solid
Epoxy out-last the competition 6 to 1
|
|
|
|